NA1100G15
PA6 Materials
Glass fiber 15% reinforced,
high flow.
| Testing Item | ASTM | Unit | Value | ||||
|---|---|---|---|---|---|---|---|
|
Tensile strength Tensile elongation |
D-638 D-638 |
Kg/cm2 % |
1150 3.5 |
||||
|
Flexural strength Flexural modulus |
D-790 |
Kg/cm2 Kg/cm 2 |
1900 53000 |
||||
|
Izod impact |
D-256 |
Kg‧cm/cm ( 23°C ) ( -30°C ) |
6.0 - |
||||
|
Heat distortion temperature |
D-648 |
°C (18.6Kg/cm 2) |
185 | ||||
| Melting point | DSC | °C | 215~225 | ||||
| Hardness | D-785 | Rockwell R | 119 | ||||
| Mold shrinkage | D-955 |
|
0.4 0.7 |
||||
| Specific gravity | D-792 | - | 1.23 | ||||
| Ash content | D-482 | % | 15(GF) | ||||
| Flammability | UL-94 | 1/16" | HB |
NYLON 6, Glass fiber 15% reinforced, high flow.
Pretreatment：23℃‚50%RH‚24hrs